| Subject: |
| Material
Properties for Above-ground Swimming Pool Vinyl |
|
|
Property
|
Test Method
|
Typical Values
|
|
Gauge
|
Micrometer
|
Various
|
±
5.0%
|
|
Width
|
Measured on Roll
|
As
ordered
|
±
¼”
|
|
Tensile Strength, psi
|
ASTM D882
|
2400
x 2100
|
Minimum
|
|
Modulus @ 100% Elongation, psi
|
ASTM D882
|
1100
x 1100
|
±
150 psi
|
|
Elongation @ Break, %
|
ASTM D882
|
300
x 300
|
Minimum
|
|
Tear Strength, gms/mil
|
ASTM D1004
|
100
x 100
|
Minimum
|
|
Low Temperature Properties
|
SPI Impact
ASTM D1790
(50% NF)
|
ŒPass -10°F
|
±
5°F
|
|
Water Extraction, % weight loss
|
ASTM D1239
|
0.35
|
Maximum
|
|
Dim. Stability, %
|
30 min. in oven @ 158°F
|
-4.0
x 1.0
|
Maximum
|
|
Hardness
|
Shore A
|
75
|
±
5
|
|
Specific Gravity
|
ASTM D792
|
1.300
|
Minimum
|
|
Volatility, %
|
ASTM D1203
24 hrs. @ 158°F
|
-1.30
|
Maximum
|
|
Contamination/
Pinholes
|
Visual
|
None
|
None
|
|
| |
Excellent resistance to Cyanuric Acid
Sodium Dichloroisocyanurate, Trichloroisocyanuric Acid, Calcium hypochlorite,
Sodium hypochlorite with 12 ppm solution. |
| |
|
| |
ŒSheeting embossed with
other than a smooth roll will have less tear strength and low temperature
impact resistance. |
| |
|
| |
Spec: S-2 |
| |
| Rev. 0-010409 |
|
|
|
| |
|
|